MP-300 organic bentonite 
 MP-300 is easily dispersed from the rheological additives of organic ammonium activated modified organic clay of smectite is the aromatics, esters, ketones and other highly polar solvents in the paint, ink rheology additives, in the second Toluene an ester (eg butyl acetate), xylene - ketones (such as the ring of ethanol), xylene, butanol, etc. --- in high polar solvent system, may increase automation activator dispersed, decentralized fineness 20um below 200 # solvent oil, white oil (mineral alcohol) and other low-level of aliphatic hydrocarbon solvent is needed to help disperse active agent (active agent 95% ethanol, organic soil weight 40-50%), MP-300 is a high anti-Shen , easily dispersed, highly transparent in the organic solvent in the bentonite. 
 Quality index: 
 Appearance White 
 Size (200 mesh)% ≥ 98 
 Moisture content% ≤ 3.5 
 Loss on ignition% ≥ 38 
 Fineness of Dispersion (xylene)% ≤ 80 
 Polar solvent polarity range 
 No glue dispersion conditions polar activator, can be added directly to dry 
 Usage: 
 The bentonite in both solvent-based paint by adding dry powder can also be used to join pre-gel. However, pre-made gels with better play to the performance and effectiveness of organic soil. For poor wetting resin systems (such as epoxy, polyester, short oil alkyd resin, etc.) use the organic bentonite, pre-made pre-gel agreeable. 
 (1) pre-gel composition: 87% solvent, 8-10% organic soil, machine of the active agent 3-4%. 
 (2) pre-gel preparation process: Solvent + organic soil (mixture stirred for 10 minutes, fully wet), then add the polar activator (stirring 5 minutes, the full expansion). 
 Other: 
 (1) have appropriate shear dispersion and the time to make organic soil fully dispersed in the solvent. 
 (2) polar additives bentonite can be easier to help the formation of lamellar some lamellar structure, and the formation of thixotropic gel, machine additives (95% ethanol, 95% methanol, 100% acetone, 95% carbonate acrylic resin), the amount normally 30-50% of organic soil. 
 (3) organic soil must have sufficient water to enable it to develop into a network structure of the pre-gel, water molecules that form a grid structure of the bridge, so easy to over-drying of organic soil, moisture content of 3.5% for the general trade, machine sex additive is not easy to use water, the polar activator content of 95% for the prone (5% water). 
 (4) In order to fully disperse the pigment, which require the added surfactant, but it must be added after the model by adding activator, or the full spread of organic soil. 
 (5) addition of organic soil is generally 0.2-2% of the total system. 
 (6) organic soil in order to ensure full dispersion, polar organic soil activator must be added after wetting in the system, not the first Canadian polar activator, added organic soil